ESAB CoreShield 6 Wire - 3/32" - 20 lb PSP VP FEMA - 242207660
Coreshield 6 is a high productivity, high deposition gasless flux cored wire. This self-shielded wire is ideal for single or multiple pass weld applications in addition to providing high deposition rates, low spatter, and good penetration. Because of its stiffer weld puddle, Coreshield 6 offers exceptional multi-pass weld stacking characteristics, produces excellent bead appearance and X-ray quality weld deposits.
Coreshield 6 is run DCEP (electrode positive).
-
Classifications/Approvals Depositions/Parameters: | 5/64 in, 2.0 mm | 275 A | 22 | 150 ipm, 381 cm/min | 6.4 lbs./hr., 2.9 kg./hr. | 78.1 % | 1 inches, 25.4 mm | | 325 A | 23 | 200 ipm, 508 cm/min | 8.5 lbs./hr., 3.8 kg./hr. | 79.6 % | 1 inches, 25.4 mm | | 390 A | 24 | 300 ipm, 762 cm/min | 12.2 lbs./hr., 5.5 kg./hr. | 80.2 % | 1 inches, 25.4 mm | | 475 A | 27 | 400 ipm, 1016 cm/min | 16.3 lbs./hr., 7.3 kg./hr. | 80.3 % | 1 inches, 25.4 mm | | 535 A | 29 | 500 ipm, 1270 cm/min | 20.7 lbs./hr., 9.3 kg./hr. | 81.2 % | 1 inches, 25.4 mm | | 600 A | 31 | 600 ipm, 1524 cm/min | 25.7 lbs./hr., 11.5 kg./hr. | 81.7 % | 1 inches, 25.4 mm | | 3/32 in, 2.4 mm | 265 A | 22 | 100 ipm, 254 cm/min | 6.1 lbs./hr., 2.9 kg./hr. | 78.7 % | 1 inches, 25.4 mm | | 365 A | 23 | 150 ipm, 381 cm/min | 9.3 lbs./hr., 4.2 kg./hr. | 79.8 % | 1 inches, 25.4 mm | | 415 A | 23 | 200 ipm, 508 cm/min | 12.5 lbs./hr., 5.6 kg./hr. | 80.9 % | 1 inches, 25.4 mm | | 530 A | 26 | 300 ipm, 762 cm/min | 19.0 lbs./hr., 8.5 kg./hr. | 81.8 % | 1 inches, 25.4 mm | | 615 A | 29 | 400 ipm, 1016 cm/min | 25.8 lbs./hr., 11.6 kg./hr. | 81.8 % | 1 inches, 25.4 mm |
Properties:
| As Welded | | | Yield Strength | 67 ksi, 465 MPa | | Tensile Strength | 85 ksi, 590 MPa | | Elongation in 2" | 26 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature -20ºF (-29ºC) | 31 ft.-lbs., 42 J | | Typical Undiluted Weld Metal Analysis | | | C | 0.12 % | | Mn | 0.8 % | | Si | 0.2 % | | P | 0.005 % | | S | 0.008 % | | Ni | 0.4 % | | Al | 0.7 % |