ESAB Dual Shield 8000-B2 Wire - 1/16" - 33 lb AWS

Dual Shield 8000-B2 is an all-position flux cored electrode which contains 1.25% Cr - 0.5% Mo. The analysis is very similar to Dual Shield 88 CM, except 8000-B2 is for out-of-position welding. The weld metal analysis is similar to an E8018-B2 low Hydrogen electrode. Dual Shield 8000-B2 wire is used for the welding of such steel as 0.5% Cr - 0.5% Mo, 1% Cr-0.5% Mo, and 1.25% Cr - 0.5% Mo. This wire is designed for single or multiple pass welding. Shielding gases of 100% CO2 and 75% Ar - Remainder CO2 may be used.

Shielding Gas

100% CO2 or Argon - CO2 mixtures up to 75% Argon

Classifications/Approvals
- AWS A5.29;E81T1-B2C/B2M
- ASME SFA 5.29

Depositions/Parameters:

Diameter	Amps	Volts	Wire Feed Speed	Deposition Rate	Efficiency
.035 in, 0.9 mm	130 A A	22	288 ipm, 732 cm/min	3.2 lbs./hr., 1.45 kg./hr.	85 %
	150 A A	25	384 ipm, 975 cm/min	4.3 lbs./hr., 1.95 kg./hr.	85 %
	200 A A	27	576 ipm, 1463 cm/min	6.5 lbs./hr., 2.95 kg./hr.	85 %
	250 A A	30	784 ipm, 1991 cm/min	8.9 lbs./hr., 4.04 kg./hr.	86 %
.045 in, 1.2 mm	150 A A	28	200 ipm, 508 cm/min	4.2 lbs./hr., 1.91 kg./hr.	86 %
	210 A A	29	300 ipm, 762 cm/min	6.3 lbs./hr., 2.86 kg./hr.	86 %
	250 A A	30	400 ipm, 1016 cm/min	8.5 lbs./hr., 3.86 kg./hr.	87 %
	290 A A	33	500 ipm, 1270 cm/min	10.7 lbs./hr., 4.85 kg./hr.	87 %
	330 A A	34	600 ipm, 1524 cm/min	12.7 lbs./hr., 5.76 kg./hr.	87 %
.052 in, 1.4 mm	155 A A	25	150 ipm, 381 cm/min	4.4 lbs./hr., 2 kg./hr.	87 %
	245 A A	28	250 ipm, 635 cm/min	7.3 lbs./hr., 3.31 kg./hr.	86 %
	310 A A	33	350 ipm, 889 cm/min	10.2 lbs./hr., 4.63 kg./hr.	85 %
	360 A A	36	450 ipm, 1143 cm/min	13.3 lbs./hr., 6.03 kg./hr.	85 %
	430 A A	37	600 ipm, 1524 cm/min	17.6 lbs./hr., 7.98 kg./hr.	87 %
1/16 in, 1.6 mm	190 A A	27	150 ipm, 38 cm/min	6.1 lbs./hr., 2.77 kg./hr.	87 %
	300 A A	30	250 ipm, 635 cm/min	10.2 lbs./hr., 4.63 kg./hr.	87 %
	365 A A	33	300 ipm, 762 cm/min	12.3 lbs./hr., 5.58 kg./hr.	86 %
	410 A A	33	350 ipm, 889 cm/min	14 lbs./hr., 6.35 kg./hr.	88 %
	450 A A	33	400 ipm, 1016 cm/min	16.1 lbs./hr., 7.3 kg./hr.	87 %
	500 A A	39	500 ipm, 1270 cm/min	20.1 lbs./hr., 9.11 kg./hr.	87 %
5/64 in, 2.0 mm	250 A A	26	112 ipm, 284 cm/min	6.4 lbs./hr., 2.9 kg./hr.	85 %
	350 A A	28	176 ipm, 447 cm/min	10.5 lbs./hr., 4.76 kg./hr.	85 %
	450 A A	31	258 ipm, 655 cm/min	14.8 lbs./hr., 6.71 kg./hr.	85 %
3/32 in, 2.4 mm	350 A A	30	124 ipm, 315 cm/min	9.6 lbs./hr., 4.35 kg./hr.	84 %
	400 A A	30	166 ipm, 422 cm/min	12.7 lbs./hr., 5.76 kg./hr.	85 %
	450 A A	31	197 ipm, 500 cm/min	15 lbs./hr., 6.8 kg./hr.	86 %
	500 A A	32	237 ipm, 602 cm/min	18.5 lbs./hr., 8.39 kg./hr.	86 %
	550 A A	34	278 ipm, 706 cm/min	21.3 lbs./hr., 9.66 kg./hr.	88 %
7/64 in, 2.8 mm	550 A A	30	140 ipm, 356 cm/min	17.1 lbs./hr., 7.76 kg./hr.	85 %
	625 A A	34	161 ipm, 409 cm/min	19.6 lbs./hr., 8.89 kg./hr.	86 %
	700 A A	36	190 ipm, 483 cm/min	23 lbs./hr., 10.43 kg./hr.	86 %
1/8 in, 3.2 mm	600 A A	32	111 ipm, 282 cm/min	16.2 lbs./hr., 7.35 kg./hr.	86 %
	725 A A	34	153 ipm, 389 cm/min	22.5 lbs./hr., 10.21 kg./hr.	86 %
	850 A A	38	194 ipm, 93 cm/min	29.2 lbs./hr., 13.25 kg./hr.	85 %

Properties:

Stress Relieved 1 hr. @ 1175ºF (635ºC) CO2
Yield Strength	83 ksi, 575 MPa
Tensile Strength	95 ksi, 650 MPa
Reduction in Area	60 %
Elongation in 2"	21 %
Typical Undiluted Weld Metal Analysis
CO2
C	0.075 %
Mn	0.5 %
Si	0.52 %
P	0.011 %
S	0.012 %
Cr	1.2 %
Mo	0.5 %

Surcharges may apply. Surcharges are billed separately!
Please call for a quote unless you agree to current market surcharges!

Return to Catalog

Categories

Shielding Gas

Classifications/Approvals