ESAB Dual Shield 8000-Ni2 Wire - .045" - 33 lb AWS - 245020409
Dual Shield 8000-Ni2 is an all-position flux cored electrode that deposits 2.5% Ni deposit with an 82 ksi (565 MPa) minimum tensile strength. Dual Shield 8000-Ni2 may be used with CO2 or Argon mixtures. The Argon-CO2 mixtures reduce spatter and further improve weldability especially for small vertical-up fillets. Dual Shield 8000-Ni2 produces superior weld metal properties which make it most desirable for such applications as shipbuilding and heavy machinery construction. The weld metal analysis is similar to an E8018-C1 low Hydrogen electrode.
Shielding Gas 100% CO2 or Argon - CO2 mixtures up to 80% Argon
-
Classifications/Approvals - ASME SFA 5.29
- A.B.S.- 3YSA
- AWS A5.29; E81T1-Ni2C/Ni2M
- MIL-E-24403/1; MIL-81T1-Ni2C/Ni2M
- CERTIFIED BY C.W.B.- AWS A5.29
Depositions/Parameters:
| .035 in, 0.9 mm | 130 A | 22 | 288 ipm, 732 cm/min | 3.2 lbs./hr., 1.45 kg./hr. | 85 % | | 150 A | 25 | 384 ipm, 975 cm/min | 4.3 lbs./hr., 1.95 kg./hr. | 85 % | | 200 A | 27 | 576 ipm, 1463 cm/min | 6.5 lbs./hr., 2.95 kg./hr. | 85 % | | 250 A | 30 | 784 ipm, 1991 cm/min | 8.9 lbs./hr., 4.04 kg./hr. | 86 % | | .045 in, 1.2 mm | 150 A | 28 | 200 ipm, 508 cm/min | 4.2 lbs./hr., 1.91 kg./hr. | 86 % | | 210 A | 29 | 300 ipm, 762 cm/min | 6.3 lbs./hr., 2.86 kg./hr. | 86 % | | 250 A | 30 | 400 ipm, 1016 cm/min | 8.5 lbs./hr., 3.86 kg./hr. | 87 % | | 290 A | 33 | 500 ipm, 1270 cm/min | 10.7 lbs./hr., 4.85 kg./hr. | 87 % | | 330 A | 34 | 600 ipm, 1524 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 87 % | | .052 in, 1.4 mm | 155 A | 25 | 150 ipm, 381 cm/min | 4.4 lbs./hr., 2.00 kg./hr. | 87 % | | 245 A | 28 | 250 ipm, 635 cm/min | 7.3 lbs./hr., 3.31 kg./hr. | 86 % | | 310 A | 33 | 350 ipm, 889 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 85 % | | 360 A | 36 | 450 ipm, 1143 cm/min | 13.3 lbs./hr., 6.03 kg./hr. | 85 % | | 430 A | 37 | 600 ipm, 1524 cm/min | 17.6 lbs./hr., 7.98 kg./hr. | 87 % | | 1/16 in, 1.6 mm | 190 A | 27 | 150 ipm, 381 cm/min | 6.1 lbs./hr., 2.77 kg./hr. | 87 % | | 300 A | 30 | 250 ipm, 635 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 87 % | | 365 A | 33 | 300 ipm, 762 cm/min | 12.3 lbs./hr., 5.58 kg./hr. | 86 % | | 410 A | 33 | 350 ipm, 889 cm/min | 14 lbs./hr., 6.35 kg./hr. | 88 % | | 450 A | 33 | 400 ipm, 1016 cm/min | 16.1 lbs./hr., 7.30 kg./hr. | 87 % | | 500 A | 39 | 500 ipm, 1270 cm/min | 20.1 lbs./hr., 9.11 kg./hr. | 87 % | | 5/64 in, 2.0 mm | 250 A | 26 | 112 ipm, 284 cm/min | 6.4 lbs./hr., 2.90 kg./hr. | 85 % | | 350 A | 28 | 176 ipm, 447 cm/min | 10.5 lbs./hr., 4.76 kg./hr. | 85 % | | 450 A | 31 | 258 ipm, 655 cm/min | 14.8 lbs./hr., 6.71 kg./hr. | 85 % | | 3/32 in, 2.4 mm | 350 A | 30 | 124 ipm, 315 cm/min | 9.6 lbs./hr., 4.35 kg./hr. | 84 % | | 400 A | 30 | 166 ipm, 422 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 85 % | | 450 A | 31 | 197 ipm, 500 cm/min | 15 lbs./hr., 6.80 kg./hr. | 86 % | | 500 A | 32 | 237 ipm, 602 cm/min | 18.5 lbs./hr., 8.39 kg./hr. | 86 % | | 550 A | 34 | 278 ipm, 706 cm/min | 21.3 lbs./hr., 9.66 kg./hr. | 88 % | | 7/64 in, 2.8 mm | 550 A | 30 | 140 ipm, 356 cm/min | 17.1 lbs./hr., 7.76 kg./hr. | 85 % | | 625 A | 34 | 161 ipm, 409 cm/min | 19.6 lbs./hr., 8.89 kg./hr. | 86 % | | 700 A | 36 | 190 ipm, 483 cm/min | 23 lbs./hr., 10.43 kg./hr. | 86 % | | 1/8 in, 3.2 mm | 600 A | 32 | 111 ipm, 282 cm/min | 16.2 lbs./hr., 7.35 kg./hr. | 86 % | | 725 A | 34 | 153 ipm, 389 cm/min | 22.5 lbs./hr., 10.21 kg./hr. | 86 % | | 850 A | 38 | 194 ipm, 493 cm/min | 29.2 lbs./hr., 13.25 kg./hr. | 85 % |
Procedures:
| As Welded 75% Ar / 25% CO2 | | | Yield Strength | 82 ksi, 565 MPa | | Tensile Strength | 90 ksi, 620 MPa | | Reduction in Area | 68 % | | Elongation in 2" | 27 % | | As Welded CO2 | | | Yield Strength | 80 ksi, 550 MPa | | Tensile Strength | 88 ksi, 605 MPa | | Reduction in Area | 67 % | | Elongation in 2" | 26 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature 0ºF (-18ºC) | | | As Welded CO2 | 62 ft.-lbs., 84 J | | As Welded 75% Ar / 25% CO2 | 63 ft.-lbs., 69 J | | Testing Temperature -20ºF (-29ºC) | | | As Welded CO2 | 43 ft.-lbs., 58 J | | As Welded 75% Ar / 25% CO2 | 47 ft.-lbs., 64 J | | Testing Temperature -40ºF (-40ºC) | | | As Welded CO2 | 39 ft.-lbs., 53 J | | As Welded 75% Ar / 25% CO2 | 40 ft.-lbs., 54 J | | Typical Undiluted Weld Metal Analysis | | | CO2 | | | C | .05 % | | Mn | 0.9 % | | Si | 0.3 % | | P | .012 % | | S | .010 % | | Ni | 2.2 % | | 75% Ar / 25% CO2 | | | C | .05 % | | Mn | 1.1 % | | Si | 0.4 % | | P | .012 % | | S | .010 % | | Ni | 2.2 % |