ESAB Dual Shield 85-C1 Wire - 3/32" - 60 lb Coil - 245005327
|
Manufacturer:
ESAB® | | SKU: |
ESA245005327
|
Price: $286.54
Order Now
|
ESAB Dual Shield 85-C1 Wire - 3/32" - 60 lb Coil - 245005327
Dual Shield 85-C1 is a basic slag multipass flux cored electrode developed to produce weld metal containing nominally 2.5% Ni with excellent mechanical properties and good notch toughness to temperatures as low as -75°F (-60°C). The weld metal meets stringent X-ray standards in both as welded and stress relieved conditions using 100% CO2 shielding gas. The thin cover of slag is easily removed, exposing flat to slightly convex weld beads. Horizontal fillets are slightly convex with equal leg lengths. The weld metal analysis is similar to an E8018-C1 low Hydrogen electrode.
-
Classifications/Approvals - ASME SFA 5.29
- AWS A5.29; E80T5-Ni2C
Depositions/Parameters:
| .045 in, 1.2 mm | 170 A A | 19 | 285 ipm, 724 cm/min | 7 lbs./hr., 3.2 kg./hr. | 96 % | 3/4 inches, 19.1 mm | | 250 A A | 30 | 469 ipm, 1191 cm/min | 10.8 lbs./hr., 4.9 kg./hr. | 91 % | 1 inches, 25.4 mm | | 300 A A | 32 | 606 ipm, 1539 cm/min | 14.2 lbs./hr., 6.44 kg./hr. | 92 % | 1 inches, 25.4 mm | | 350 A A | 32 | 740 ipm, 1880 cm/min | 17.5 lbs./hr., 7.94 kg./hr. | 93 % | 1 inches, 25.4 mm | | 1/16 in, 1.6 mm | 300 A A | 30 | 226 ipm, 574 cm/min | 9.8 lbs./hr., 4.45 kg./hr. | 92 % | 1 inches, 25.4 mm | | 400 A A | 32 | 369 ipm, 937 cm/min | 16.1 lbs./hr., 7.3 kg./hr. | 92 % | 1 inches, 25.4 mm | | 450 A A | 32 | 422 ipm, 1072 cm/min | 18.5 lbs./hr., 8.4 kg./hr. | 93 % | 1 inches, 25.4 mm | | 3/32 in, 2.4 mm | 450 A A | 32 | 217 ipm, 551 cm/min | 17.6 lbs./hr., 8 kg./hr. | 85 % | 1 inches, 25.4 mm | | 475 A A | 32 | 245 ipm, 622 cm/min | 20 lbs./hr., 9.1 kg./hr. | 87 % | 1 inches, 25.4 mm | | 500 A A | 32 | 270 ipm, 686 cm/min | 22.8 lbs./hr., 10.3 kg./hr. | 89 % | 1 inches, 25.4 mm | | 550 A A | 33 | 346 ipm, 879 cm/min | 29.6 lbs./hr., 13.4 kg./hr. | 91 % | 1 inches, 25.4 mm |
Properties:
| As Welded CO2 | | | Yield Strength | 71 ksi, 490 MPa | | Tensile Strength | 85 ksi, 585 MPa | | Reduction in Area | 56 % | | Elongation in 2" | 23 % | | Stress Relieved 1 hr. @ 1150ºF (621ºC) CO2 | | | Yield Strength | 70 ksi, 485 MPa | | Tensile Strength | 84 ksi, 580 MPa | | Reduction in Area | 67 % | | Elongation in 2" | 30 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature -75ºF (-60ºC) | | | As Welded CO2 | 51 ft.-lbs., 69 J | | Stress Relieved 1 hr. @ 1150ºF (621ºC) CO2 | 62 ft.-lbs., 84 J | | Typical Undiluted Weld Metal Analysis | | | CO2 | | | C | .05 % | | Mn | 1.1 % | | Si | 0.4 % | | P | 0.007 % | | S | .011 % | | Ni | 2.2 % |