ESAB Dual Shield II 110 Wire - .045" - 33 lb PSP VP - 245013693

ESAB Dual Shield II 110 Wire - .045" - 33 lb PSP VP - 245013693

Manufacturer: ESAB®
SKU: ESA245013693
Price: $221.90
Order Now

Quantity:


ESAB Dual Shield II 110 Wire - .045" - 33 lb PSP VP - 245013693

Dual Shield II 110 is an all-position flux cored electrode which produces a smooth spray-like transfer, low spatter levels, low diffusible hydrogen levels, easy slag removal and good arc direction. Dual Shield II 110 was designed to join high strength steel such as HY-100 and T-1 in the as welded or stress relieved condition using 75% Ar / 25% CO2 shielding gas. It is well suited for joining high tensile steels that will be used in low temperatures. The weld metal analysis is similar to an E11018-M low hydrogen electrode.

Shielding Gas

75% Argon/25% CO2
100% CO2


  • Classifications/Approvals

    • A.B.S.- AWS A5.29; E111T1-K3M
    • AWS A5.29; E111T1-K3CH4/K3MH4
    • ASME SFA 5.29

Depositions/Parameters:

Diameter Amps Volts Wire Feed Speed Deposition Rate Efficiency
.045 in, 1.2 mm 150 A A 28 200 ipm, 508 cm/min 4.2 lbs./hr., 1.91 kg./hr. 86 %
210 A A 29 300 ipm, 762 cm/min 6.3 lbs./hr., 2.86 kg./hr. 86 %
250 A A 30 400 ipm, 1016 cm/min 8.5 lbs./hr., 3.86 kg./hr. 87 %
290 A A 33 500 ipm, 1270 cm/min 10.7 lbs./hr., 4.85 kg./hr. 87 %
330 A A 34 600 ipm, 1524 cm/min 12.7 lbs./hr., 5.76 kg./hr. 87 %
.052 in, 1.4 mm 155 A A 25 150 ipm, 381 cm/min 4.4 lbs./hr., 2 kg./hr. 87 %
245 A A 28 250 ipm, 635 cm/min 7.3 lbs./hr., 3.31 kg./hr. 86 %
310 A A 33 350 ipm, 889 cm/min 10.2 lbs./hr., 4.63 kg./hr. 85 %
360 A A 36 450 ipm, 1143 cm/min 13.3 lbs./hr., 6.03 kg./hr. 85 %
430 A A 37 600 ipm, 1524 cm/min 17.6 lbs./hr., 7.98 kg./hr. 87 %
1/16 in, 1.6 mm 190 A A 27 150 ipm, 38 cm/min 6.1 lbs./hr., 2.77 kg./hr. 87 %
300 A A 30 250 ipm, 635 cm/min 10.2 lbs./hr., 4.63 kg./hr. 87 %
365 A A 33 300 ipm, 762 cm/min 12.3 lbs./hr., 5.58 kg./hr. 86 %
410 A A 33 350 ipm, 889 cm/min 14 lbs./hr., 6.35 kg./hr. 88 %
450 A A 33 400 ipm, 1016 cm/min 16.1 lbs./hr., 7.3 kg./hr. 87 %
500 A A 39 500 ipm, 1270 cm/min 20.1 lbs./hr., 9.11 kg./hr. 87 %


Properties:

As Welded 75% Ar / 25% CO2  
Yield Strength 110 ksi, 760 MPa
Tensile Strength 120 ksi, 830 MPa
Reduction in Area 54 %
Elongation in 2" 19 %
Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2  
Yield Strength 108 ksi, 745 MPa
Tensile Strength 116 ksi, 800 MPa
Reduction in Area 56 %
Elongation in 2" 19 %
Typical Charpy V-Notch Impact Properties  
Testing Temperature 0ºF (-18ºC)  
As Welded 75% Ar / 25% CO2 40 ft.-lbs., 54 J
Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 29 ft.-lbs., 39 J
Testing Temperature -20ºF (-29ºC)  
As Welded 75% Ar / 25% CO2 36 ft.-lbs., 49 J
Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 27 ft.-lbs., 37 J
Testing Temperature -60ºF (-51ºC)  
As Welded 75% Ar / 25% CO2 26 ft.-lbs., 35 J
Stress Relieved 8 hrs. @ 1150ºF (621ºC) 75% Ar / 25% CO2 21 ft.-lbs., 28 J
Typical Undiluted Weld Metal Analysis  
75% Ar / 25% CO2  
C .05 %
Mn 1.91 %
Si .43 %
P .013 %
S .010 %
Ni 1.74 %
Mo 0.39 %