ESAB Coreweld 80-D2 Wire - 1/16" - 600 lb OMP - 243415296
Coreweld 80-D2 is a metal cored wire equivalent to ER80S-D2 solid wire. Coreweld 80-D2 produces higher deposition rates, better wetting action, with an absence of copper coating on the wire. Coreweld 80-D2 was developed for HSLA steels. This product is capable of single or multiple pass welding
Shielding Gas 75% Ar / 25% CO2
-
Classifications/Approvals - AWS A5.28; E80C-G
- ASME SFA 5.28
Depositions/Parameters:
| .035 in, 0.9 mm | 150 A | 25 V | 320 ipm, 813 cm/min | 4.4 lbs./hr., 1.2 kg./hr. | 92 % | | 200 A | 27 V | 472 ipm, 1199 cm/min | 6.5 lbs./hr., 2.95 kg./hr. | 92 % | | 250 A | 29 V | 680 ipm, 1727 cm/min | 9.4 lbs./hr., 4.26 kg./hr. | 92 % | | .045 in, 1.2 mm | 250 A | 28 V | 330 ipm, 838 cm/min | 8.0 lbs./hr., 3.63 kg./hr. | 90 % | | 275 A | 30 V | 430 ipm, 1092 cm/min | 11.1 lbs./hr., 5.03 kg./hr. | 94 % | | 300 A | 32 V | 464 ipm, 1179 cm/min | 11.6 lbs./hr., 5.26 kg./hr. | 94 % | | 350 A | 32 V | 512 ipm, 1300 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 96 % | | .052 in, 1.4 mm | 275 A | 29 V | 262 ipm, 665 cm/min | 8.0 lbs./hr., 3.63 kg./hr. | 92 % | | 300 A | 29 V | 312 ipm, 792 cm/min | 9.6 lbs./hr., 4.35 kg./hr. | 93 % | | 325 A | 30 V | 328 ipm, 833 cm/min | 10.1 lbs./hr., 4.58 kg./hr. | 93 % | | 1/16 in, 1.6 mm | 300 A | 30 V | 181 ipm, 460 cm/min | 8.6 lbs./hr., 3.90 kg./hr. | 89 % | | 350 A | 30 V | 241 ipm, 612 cm/min | 11.9 lbs./hr., 5.40 kg./hr. | 94 % | | 400 A | 32 V | 293 ipm, 744 cm/min | 14.6 lbs./hr., 6.62 kg./hr. | 94 % | | 450 A | 34 V | 333 ipm, 846 cm/min | 16.2 lbs./hr., 7.35 kg./hr. | 94 % | | 5/64 in, 2.0 mm | 350 A | 27 V | 160 ipm, 406 cm/min | 11.6 lbs./hr., 5.26 kg./hr. | 94 % | | 400 A | 28 V | 185 ipm, 470 cm/min | 13.2 lbs./hr., 5.99 kg./hr. | 95 % | | 450 A | 28 V | 210 ipm, 533 cm/min | 15.8 lbs./hr., 7.17 kg./hr. | 97 % | | 500 A | 29 V | 280 ipm, 711 cm/min | 20.4 lbs./hr., 9.25 kg./hr. | 97 % | | 3/32 in, 2.4 mm | 400 A | 31 V | 115 ipm, 292 cm/min | 11.5 lbs./hr., 5.22 kg./hr. | 95 % | | 450 A | 31 V | 138 ipm, 350 cm/min | 14.5 lbs./hr., 6.58 kg./hr. | 97 % | | 500 A | 32 V | 155 ipm, 394 cm/min | 16.5 lbs./hr., 7.48 kg./hr. | 97 % | | 550 A | 32 V | 197 ipm, 500 cm/min | 21.0 lbs./hr., 9.53 kg./hr. | 98 % |
Properties:
| As Welded 75% Ar / 25% CO2 | | | Yield Strength | 77 ksi, 530 MPa | | Tensile Strength | 90 ksi, 620 MPa | | Reduction in Area | 62 % | | Elongation in 2" | 26 % | | Stress Relieved 8 hrs. @ 1175ºF (635ºC) 75% Ar / 25% CO2 Gas | | | Yield Strength | 77 ksi, 530 MPa | | Tensile Strength | 90 ksi, 625 MPa | | Reduction in Area | 68 % | | Elongation in 2" | 26 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature -20ºF (-29ºC) | | | As Welded 75% Ar / 25% CO2 | 34 ft.-lbs., 46 J | | Stress Relieved 8 hrs. @ 1175ºF (635ºC) CO2 | 25 ft.-lbs., 34 J | | Testing Temperature -40ºF (-40ºC) | | | As Welded 75% Ar / 25% CO2 | 23 ft.-lbs., 31 J | | Typical Undiluted Weld Metal Analysis | | | 75% Ar / 25% CO2 | | | C | 0.09 % | | Mn | 1.2 % | | Si | 0.3 % | | P | 0.010 % | | S | 0.018 % | | Mo | 0.4 % |