ESAB Coreweld 110 Wire - .052" - 600 lb OMP - 243416146
Coreweld 110 is a metal cored electrode designed for single and multipass welding of high strength low alloy steels, such as T-1, HY-80, and HY-100. The arc is smooth with virtually no spatter. Coreweld 110 is recommended for welding quenched and tempered high strength steels. Because of the metallic core, the wire offers both the high deposition rates of a flux cored electrode and the high efficiencies of a solid wire.
Shielding Gas 92% Argon / 8% CO2
-
Classifications/Approvals - ASME SFA 5.28
- AWS A5.28; E110C-G
Depositions/Parameters:
| .035 in, 0.9 mm | 150 A | 25 V | 320 ipm, 813 cm/min | 4.4 lbs./hr., 1.2 kg./hr. | 92 % | | 200 A | 27 V | 472 ipm, 1199 cm/min | 6.5 lbs./hr., 2.95 kg./hr. | 92 % | | 250 A | 29 V | 680 ipm, 1727 cm/min | 9.4 lbs./hr., 4.26 kg./hr. | 92 % | | .045 in, 1.2 mm | 250 A | 28 V | 330 ipm, 838 cm/min | 8.0 lbs./hr., 3.63 kg./hr. | 90 % | | 275 A | 30 V | 430 ipm, 1092 cm/min | 11.1 lbs./hr., 5.03 kg./hr. | 94 % | | 300 A | 32 V | 464 ipm, 1179 cm/min | 11.6 lbs./hr., 5.26 kg./hr. | 94 % | | 350 A | 32 V | 512 ipm, 1300 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 96 % | | .052 in, 1.4 mm | 275 A | 29 V | 262 ipm, 665 cm/min | 8.0 lbs./hr., 3.63 kg./hr. | 92 % | | 300 A | 29 V | 312 ipm, 792 cm/min | 9.6 lbs./hr., 4.35 kg./hr. | 93 % | | 325 A | 30 V | 328 ipm, 833 cm/min | 10.1 lbs./hr., 4.58 kg./hr. | 93 % | | 1/16 in, 1.6 mm | 300 A | 30 V | 181 ipm, 460 cm/min | 8.6 lbs./hr., 3.90 kg./hr. | 89 % | | 350 A | 30 V | 241 ipm, 612 cm/min | 11.9 lbs./hr., 5.40 kg./hr. | 94 % | | 400 A | 32 V | 293 ipm, 744 cm/min | 14.6 lbs./hr., 6.62 kg./hr. | 94 % | | 450 A | 34 V | 333 ipm, 846 cm/min | 16.2 lbs./hr., 7.35 kg./hr. | 94 % | | 5/64 in, 2.0 mm | 350 A | 27 V | 160 ipm, 406 cm/min | 11.6 lbs./hr., 5.26 kg./hr. | 94 % | | 400 A | 28 V | 185 ipm, 470 cm/min | 13.2 lbs./hr., 5.99 kg./hr. | 95 % | | 450 A | 28 V | 210 ipm, 533 cm/min | 15.8 lbs./hr., 7.17 kg./hr. | 97 % | | 500 A | 29 V | 280 ipm, 711 cm/min | 20.4 lbs./hr., 9.25 kg./hr. | 97 % | | 3/32 in, 2.4 mm | 400 A | 31 V | 115 ipm, 292 cm/min | 11.5 lbs./hr., 5.22 kg./hr. | 95 % | | 450 A | 31 V | 138 ipm, 350 cm/min | 14.5 lbs./hr., 6.58 kg./hr. | 97 % | | 500 A | 32 V | 155 ipm, 394 cm/min | 16.5 lbs./hr., 7.48 kg./hr. | 97 % | | 550 A | 32 V | 197 ipm, 500 cm/min | 21.0 lbs./hr., 9.53 kg./hr. | 98 % |
Properties:
| As Welded 92% Ar / 8% CO2 | | | Yield Strength | 113 ksi, 770 MPa | | Tensile Strength | 121 ksi, 835 MPa | | Elongation in 2" | 20 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature 0ºF (-18ºC) | | | As Welded 92% Ar / 8% CO2 | 35 ft.-lbs., 47 J | | Testing Temperature -60ºF (-51ºC) | | | As Welded 92% Ar / 8% CO2 | 30 ft.-lbs., 41 J | | Typical Undiluted Weld Metal Analysis | | | 92% Ar / 8% CO2 | | | C | 0.05 % | | Mn | 1.6 % | | Si | 0.3 % | | P | 0.016 % | | S | 0.013 % | | Cr | 0.1 % | | Ni | 2.5 % | | Mo | 0.6 % |