ESAB Cryo-Shield 308L Wire - .035" - 33 lb PSP VP - 252210026
Cryo-Shield 308L is an all-position wire adaptable to a variety of shop and field erection applications. The use of argon/CO2 gas shielding is recommended for maximum toughness. Designed for cryogenic applications where good weld metal toughness is required. Applications include cryogenic vessel fabrication and process piping repair. Cyro-Shield 308L is guaranteed to produce a minimum of 15mils lateral expansion at -320ºF.
Cryo-Shield 308L was developed for the welding of types 304 & 304L stainless steels for the low temperature service, even down to liquid helium temperatures. This is done by controlling the composition and the ferrite content to give good toughness at temperatures of -320ºF (-196ºC) and lower.
Cryo-Shield 308L was developed for welding in all positions and performs particularly well in the vertical position with excellent slag removal.
* This item is subject to Industry Alloy Surcharges
Shielding Gas 75-80% Ar/Bal CO2 -
Classifications/Approvals - ASME IX F No. 6
- ASME II SFA 5.22 E308LT1-1/LT1-4
Depositions/Parameters: | .035 in, 0.9 mm | 100 A | 23 | 265 ipm, 6.7 cm/min | 2.9 lbs./hr., 1.3 kg./hr. | 83.9 % | | 120 A | 23 | 315 ipm, 8.0 cm/min | 3.4 lbs./hr., 1.5 kg./hr. | 81.4 % | | 140 A | 25 | 405 ipm, 10.3 cm/min | 4.6 lbs./hr., 2.1 kg./hr. | 82.6 % | | 170 A | 26 | 530 ipm, 13.5 cm/min | 5.7 lbs./hr., 2.6 kg./hr. | 81.8 % | | .045 in, 1.2 mm | 130 A | 25 | 227 ipm, 5.8 cm/min | 4.25 lbs./hr., 1.9 kg./hr. | 84.0 % | | 165 A | 26 | 341 ipm, 8.7 cm/min | 6.14 lbs./hr., 2.8 kg./hr. | 83.0 % | | 190 A | 28 | 445 ipm, 11.3 cm/min | 8.08 lbs./hr., 3.7 kg./hr. | 84.0 % | | 220 A | 30 | 567 ipm, 14.4 cm/min | 10.24 lbs./hr., 4.6 kg./hr. | 84.0 % | | .062 in, 1.6 mm | 170 A | 25 | 154 ipm, 3.9 cm/min | 5.34 lbs./hr., 2.4 kg./hr. | 83.0 % | | 210 A | 27 | 193 ipm, 4.9 cm/min | 6.89 lbs./hr., 3.1 kg./hr. | 82.5 % | | 250 A | 28 | 243 ipm, 6.2 cm/min | 8.57 lbs./hr., 3.9 kg./hr. | 83.0 % | | 300 A | 29 | 321 ipm, 8.2 cm/min | 11.43 lbs./hr., 5.2 kg./hr. | 83.0 % | Properties: | As Welded using 75% Ar - 25% CO2 | | | Tensile Strength | 80 ksi, 550 MPa | | Yield Strength | 65 ksi, 450 MPa | | Elongation in 2" | 45 % | | Typical Undiluted Weld Metal Analysis | | | 75% Ar / 25% CO2 | | | C | 0.03% | | Mn | 1.3% | | Si | 0.8% | | Cr | 19% | | Ni | 10.7% | | Mo | 0.1% | | Cu | 0.15% | | Ferrite | 4% FN |