ESAB Shield-Bright 309LMo X-tra Wire - .045" - 33 lb PSP VP - 252200969
Shield-Bright 309LMo X-tra was developed for the welding of stainless steels to carbon or low alloy steels. For thick sections it is often preferable that the non-stainless steel should be buttered with a layer of Shield-Bright 309L X-tra and the joint made with Shield-Bright 316L X-tra or 308L X-tra. It was also developed for the first layer cladding of carbon and low alloy steels prior to subsequent layers from Shield-Bright 316L X-tra or 317L X-tra.
The service temperature of all the resulting weldments should not exceed about 700ºF (370ºC). Multiple layer cladding with Shield-Bright 309LMo X-tra can be used for additional corrosion resistance in some applications in the pulp and paper industry. Shield-Bright 309LMo X-tra was developed for welding in the flat position and for horizontal fillet welds with flat to concave beads with excellent slag removal. It can be used with either 75% Ar / 25% CO2 or 100% CO2 gases.
* This item is subject to Industry Alloy Surcharges
Designed for welding type 316 clad steels on the first pass in cladding steels or for welding dissimilar metals such as molybdenum-containing austenitic stainless steels to carbon steels. Used in paper mills and in power plants. Carbon content 0.04% maximum.
-
Classifications/Approvals - ASME IX F No. 6
- ASME II SFA 5.22 E309LMoT0-1/T0-4
- AWS A5.22 E309LMoT0-1 & E309LMoT0-4
Depositions/Parameters:
| .035 in, 0.9 mm | 120 A | 23 | 315 ipm, 8 cm/min | 3.4 lbs./hr., 1.5 kg./hr. | 81.4 % | 1/2 - 1 inches, 12.5 - 25 mm | | 140 A | 25 | 405 ipm, 10.3 cm/min | 4.6 lbs./hr., 2.1 kg./hr. | 82.6 % | 1/2 - 1 inches, 12.5 - 25 mm | | 170 A | 26 | 530 ipm, 13.5 cm/min | 5.7 lbs./hr., 2.6 kg./hr. | 81.8 % | 1/2 - 1 inches, 12.5 - 25 mm | | .045 in, 1.2 mm | 150 A | 25 | 259 ipm, 6.6 cm/min | 5 lbs./hr., 2.3 kg./hr. | 83.9 % | 1/2 - 1 inches, 12.5 - 25 mm | | 200 A | 29 | 410 ipm, 10.4 cm/min | 7.7 lbs./hr., 3.5 kg./hr. | 84.2 % | 1/2 - 1 inches, 12.5 - 25 mm | | 300 A | 33 | 860 ipm, 21.9 cm/min | 16.9 lbs./hr., 7.7 kg./hr. | 87 % | 1/2 - 1 inches, 12.5 - 25 mm | | 1/16 in, 1.6 mm | 200 A | 25 | 172 ipm, 4.4 cm/min | 6.7 lbs./hr., 3.1 kg./hr. | 83.6 % | 1/2 - 1 inches, 12.5 - 25 mm | | 240 A | 28 | 225 ipm, 5.7 cm/min | 8.1 lbs./hr., 3.7 kg./hr. | 83.6 % | 1/2 - 1 inches, 12.5 - 25 mm | | 400 A | 33 | 495 ipm, 12.58 cm/min | 18.9 lbs./hr., 8.6 kg./hr. | 85.5 % | 1/2 - 1 inches, 12.5 - 25 mm |
Properties:
| As Welded 75% Ar / 25% CO2 | | | Tensile Strength | 100 ksi, 690 MPa | | Yield Strength | 80 ksi, 550 MPa | | Elongation in 2" | 30 % | | Typical Undiluted Weld Metal Analysis | | | As Welded CO2 | | | C | 0.03 % | | Mn | 1.5 % | | Si | 0.5 % | | Cr | 23.5 % | | Ni | 13.5 % | | Mo | 2.5 % | | Cu | 0.1 % | | Ferrite | 19 FN | | As Welded 75% Ar / 25% CO2 | | | C | 0.03 % | | Mn | 1.6 % | | Si | 0.6 % | | Cr | 23.5 % | | Ni | 13.5 % | | Mo | 2.5 % | | Cu | 0.1 % | | Ferrite | 20 FN |