ESAB Shield-Bright 309L Wire - .035" - 33 lb PSP VP - 252200415
Shield-Bright 309L was developed for welding stainless steel to carbon or low alloy steels and for the first layer cladding of carbon and low alloy steels. It was designed for welding in all positions and performs particularly well in the vertical position with excellent slag removal.
For joining thick sections, it is perferred the non-stainless steel be buttered with a layer of Shield-Bright 309L and the joint completed with Shield-Bright 316L or 308L. The service temperature should not exceed approximately 750ºF(399ºC).
* This item is subject to Industry Alloy Surcharges
Shielding Gas 75%Ar / 25%CO2 or 100%CO2
-
Classifications/Approvals - G.L.- AWS A5.22; E309LT1-4
- ASME IX F No. 6
- MIL-STD-1689 APPLICATIONS-NAVY
- TUV
- ASME II SFA 5.22 E309LT1-1/T1-4
- CERTIFIED BY C.W.B.- AWS A5.22
Depositions/Parameters:
| .035 in, 0.9 mm | 100 A | 23 | 265 ipm, 6.7 cm/min | 2.9 lbs./hr., 1.3 kg./hr. | 83.9 % | 1/2 - 1 inches, 12.5 - 25 mm | | 120 A | 23 | 315 ipm, 8 cm/min | 3.4 lbs./hr., 1.5 kg./hr. | 81.4 % | 1/2 - 1 inches, 12.5 - 25 mm | | 140 A | 25 | 405 ipm, 10.3 cm/min | 4.6 lbs./hr., 2.1 kg./hr. | 82.6 % | 1/2 - 1 inches, 12.5 - 25 mm | | 170 A | 26 | 530 ipm, 13.5 cm/min | 5.7 lbs./hr., 2.6 kg./hr. | 81.8 % | 1/2 - 1 inches, 12.5 - 25 mm | | .045 in, 1.2 mm | 130 A | 25 | 227 ipm, 5.8 cm/min | 4.25 lbs./hr., 1.9 kg./hr. | 84 % | 1/2 - 1 inches, 12.5 - 25 mm | | 165 A | 26 | 341 ipm, 8.7 cm/min | 6.14 lbs./hr., 2.8 kg./hr. | 83 % | 1/2 - 1 inches, 12.5 - 25 mm | | 190 A | 28 | 445 ipm, 11.3 cm/min | 8.08 lbs./hr., 3.7 kg./hr. | 84 % | 1/2 - 1 inches, 12.5 - 25 mm | | 220 A | 30 | 567 ipm, 14.4 cm/min | 10.24 lbs./hr., 4.6 kg./hr. | 84 % | 1/2 - 1 inches, 12.5 - 25 mm | | 1/16 in, 1.6 mm | 170 A | 25 | 154 ipm, 3.9 cm/min | 5.34 lbs./hr., 2.4 kg./hr. | 83 % | 1/2 - 1 inches, 12.5 - 25 mm | | 210 A | 27 | 193 ipm, 4.9 cm/min | 6.89 lbs./hr., 3.1 kg./hr. | 82.5 % | 1/2 - 1 inches, 12.5 - 25 mm | | 250 A | 28 | 243 ipm, 6.2 cm/min | 8.57 lbs./hr., 3.9 kg./hr. | 83 % | 1/2 - 1 inches, 12.5 - 25 mm | | 300 A | 29 | 321 ipm, 8.2 cm/min | 11.43 lbs./hr., 5.2 kg./hr. | 83 % | 1/2 - 1 inches, 12.5 - 25 mm |
Properties:
| As Welded 75% Ar / 25% CO2 | | | Tensile Strength | 87 ksi, 600 MPa | | Yield Strength | 70 ksi, 480 MPa | | Elongation in 2" | 35 % | | Typical Undiluted Weld Metal Analysis | | | As Welded CO2 | | | C | 0.03 % | | Mn | 1.2 % | | Si | 0.9 % | | Cr | 23.5 % | | Ni | 12.5 % | | Mo | 0.1 % | | Cu | 0.1 % | | Ferrite | 16 FN | | As Welded 75% Ar / 25% CO2 | | | C | 0.03 % | | Mn | 1.3 % | | Si | 0.9 % | | Cr | 24 % | | Ni | 12.5 % | | Mo | 0.1 % | | Cu | 0.1 % | | Ferrite | 18 FN |