Spoolarc 75 is a copper-coated 1% nickel solid wire for carbon steel and low alloy welding applications using either the MIG/Gas Metal Arc Welding (GMAW) or Submerged Arc Welding (SAW) processes. Spoolarc 75 produces a deposit that meets the weathering requirements of AWS D1.1 and D1.5 and is designed to weld weathering steels and/or where improved low temperature impact toughness is specified. Shielding gas choices for Spoolarc 75 are Ar/CO2 mixtures containing a minimum of 75% Ar or the 98% Ar/2% O2. In the SAW mode, Spoolarc 75 is typically used with a neutral flux such as ESAB OK Flux 429, 10.71, and 10.62. Spoolarac 75 is used for bridge and structural welding.
-
Classifications/Approvals - AWS/ASME SFA 5.28; ER80S-Ni1
- AWS/ASME SFA 5.23 ENi1K
Depositions/Parameters:
Spray Transfer Deposition Table | .023 in, 0.6 mm | 400 ipm, 1016 cm/min | 100 | 23 | 2.7 lbs./hr., 1.2 kg./hr. | | 450 ipm, 1143 cm/min | 106 | 23 | 3.1 lbs./hr., 1.4 kg./hr. | | 500 ipm, 1270 cm/min | 111 | 24 | 3.4 lbs./hr., 1.6 kg./hr. | | 550 ipm, 1397 cm/min | 117 | 24 | 3.8 lbs./hr., 1.7 kg./hr. | | 600 ipm, 1524 cm/min | 122 | 25 | 4.1 lbs./hr., 1.9 kg./hr. | | 630 ipm, 1600 cm/min | 125 | 25 | 4.3 lbs./hr., 2 kg./hr. | | .030 in, 0.8 mm | 500 ipm, 1270 cm/min | 160 | 24 | 5.8 lbs./hr., 2.6 kg./hr. | | 550 ipm, 1397 cm/min | 173 | 25 | 6.4 lbs./hr., 2.9 kg./hr. | | 600 ipm, 1524 cm/min | 187 | 25 | 7 lbs./hr., 3.2 kg./hr. | | 650 ipm, 1651 cm/min | 200 | 26 | 7.6 lbs./hr., 3.4 kg./hr. | | .035 in, 0.9 mm | 400 ipm, 1016 cm/min | 180 | 25 | 6.3 lbs./hr., 2.9 kg./hr. | | 450 ipm, 1143 cm/min | 197 | 26 | 7.1 lbs./hr., 3.2 kg./hr. | | 500 ipm, 1270 cm/min | 213 | 26 | 7.9 lbs./hr., 3.6 kg./hr. | | 550 ipm, 1397 cm/min | 230 | 27 | 8.7 lbs./hr., 4 kg./hr. | | .045 in, 1.2 mm | 300 ipm, 762 cm/min | 260 | 25 | 7.9 lbs./hr., 3.6 kg./hr. | | 350 ipm, 889 cm/min | 280 | 26 | 9.2 lbs./hr., 4.2 kg./hr. | | 400 ipm, 1016 cm/min | 300 | 28 | 10.5 lbs./hr., 4.8 kg./hr. | | 450 ipm, 1143 cm/min | 320 | 29 | 11.8 lbs./hr., 5.4 kg./hr. | | 500 ipm, 1270 cm/min | 340 | 30 | 13.1 lbs./hr., 6 kg./hr. | | .052 in, 1.3 mm | 265 ipm, 673 cm/min | 275 | 26 | 9.3 lbs./hr., 4.2 kg./hr. | | 300 ipm, 762 cm/min | 310 | 28 | 10.5 lbs./hr., 4.8 kg./hr. | | 350 ipm, 889 cm/min | 360 | 31 | 12.2 lbs./hr., 5.6 kg./hr. | | 390 ipm, 991 cm/min | 400 | 33 | 13.6 lbs./hr., 6.2 kg./hr. | | .062 in, 1.6 mm | 180 ipm, 457 cm/min | 290 | 26 | 9.1 lbs./hr., 4.1 kg./hr. | | 200 ipm, 508 cm/min | 310 | 28 | 10.1 lbs./hr., 4.6 kg./hr. | | 230 ipm, 584 cm/min | 340 | 31 | 11.6 lbs./hr., 5.3 kg./hr. | | 260 ipm, 660 cm/min | 370 | 34 | 13.2 lbs./hr., 6 kg./hr. | | 280 ipm, 711 cm/min | 390 | 36 | 14.2 lbs./hr., 6.4 kg./hr. |
Shortarc Transfer Deposition Table | .023 in, 0.6 mm | 150 ipm, 381 cm/min | 45 | 14 | 1 lbs./hr., 0.4 kg./hr. | | 200 ipm, 508 cm/min | 55 | 14 | 1.3 lbs./hr., 0.6 kg./hr. | | 250 ipm, 635 cm/min | 65 | 15 | 1.6 lbs./hr., 0.7 kg./hr. | | 300 ipm, 762 cm/min | 74 | 15 | 2 lbs./hr., 0.9 kg./hr. | | 350 ipm, 889 cm/min | 84 | 16 | 2.3 lbs./hr., 1 kg./hr. | | 380 ipm, 965 cm/min | 90 | 16 | 2.5 lbs./hr., 1.1 kg./hr. | | .030 in, 0.8 mm | 150 ipm, 381 cm/min | 60 | 14 | 1.7 lbs./hr., 0.8 kg./hr. | | 200 ipm, 508 cm/min | 80 | 15 | 2.2 lbs./hr., 1 kg./hr. | | 250 ipm, 635 cm/min | 100 | 15 | 2.8 lbs./hr., 1.3 kg./hr. | | 300 ipm, 762 cm/min | 120 | 16 | 3.3 lbs./hr., 1.5 kg./hr. | | 350 ipm, 889 cm/min | 140 | 16 | 3.9 lbs./hr., 1.8 kg./hr. | | 360 ipm, 914 cm/min | 144 | 16 | 4 lbs./hr., 1.8 kg./hr. | | .035 in, 0.9 mm | 180 ipm, 457 cm/min | 90 | 15 | 2.7 lbs./hr., 1.2 kg./hr. | | 220 ipm, 559 cm/min | 113 | 16 | 3.3 lbs./hr., 1.5 kg./hr. | | 260 ipm, 660 cm/min | 137 | 18 | 4 lbs./hr., 1.8 kg./hr. | | 300 ipm, 762 cm/min | 160 | 19 | 4.6 lbs./hr., 2.1 kg./hr. | | .045 in, 1.2 mm | 125 ipm, 318 cm/min | 130 | 17 | 3.1 lbs./hr., 1.4 kg./hr. | | 160 ipm, 406 cm/min | 163 | 18 | 4 lbs./hr., 1.8 kg./hr. | | 200 ipm, 508 cm/min | 200 | 19 | 5 lbs./hr., 2.3 kg./hr. | | .052 in, 1.3 mm | 135 ipm, 343 cm/min | 150 | 17 | 4.5 lbs./hr., 2.1 kg./hr. | | 160 ipm, 406 cm/min | 173 | 18 | 5.4 lbs./hr., 2.4 kg./hr. | | 190 ipm, 483 cm/min | 200 | 20 | 6.4 lbs./hr., 2.9 kg./hr. |
Properties:
| As Welded GMAW 98% Ar / 2% O2 | | | Yield Strength | 70 ksi, 485 MPa | | Tensile Strength | 81 ksi, 560 MPa | | Elongation in 2" | 31 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature -50°F (-46°C) | | | As Welded GMAW 98% Ar / 2% O2 | 98 ft.-lbs., 133 J | | Typical Undiluted Weld Metal Analysis | | | GMAW 98% Ar / 2% O2 | | | C | 0.08 % | | Mn | 0.9 % | | Si | 0.4 % | | P | 0.008 % | | S | 0.007 % | | Ni | 0.8 % | | Typical Wire Analysis | | | C | 0.08 % | | Mn | 1.0 % | | Si | 0.5 % | | P | 0.006 % | | S | 0.008 % | | Ni | 0.9 % | | Wire Chemistries | | | C | 0.07 % | | Mn | 1.13 % | | Si | 0.49 % | | P | 0.005 % | | S | 0.005 % | | Ni | 0.90 % |