ESAB Arcaloy ER308L Welding Wire - .045" - 33 lb BAWS - 258014513
Arcaloy ER308L has good general corrosion resistance. This alloy has a low carbon content which makes this alloy particularly recommended where there is a risk of intergranular corrosion. Arcaloy ER308L is also for joining 18% Cr - 8% Ni type and Nb-stabilized steels of the same type, assuming the service temperature will not exceed 662°F (350°C).
* This item is subject to Industry Alloy Surcharges
-
Classifications/Approvals - ASME II SFA 5.9 ER308/308L
- AWS A5.9; ER308/308L
- Certified by CWB - AWS A5.9; ER308/308L
- ASME IX F No. 6
- QPL-19933; MIL-308L
- A.B.S.- AWS A5.9; ER308/308L
Depositions/Parameters:
Short Circuit Transfer Table | .030 in., 0.8 mm | 156-312 ipm, 396-792 cm/min | 40-120 | 15-20 | 1.4-3.8 lbs./hr., 0.64-1.72 kg/hr | | .035 in., 0.9 mm | 156-312 ipm, 396-792 cm/min | 60-140 | 15-21 | 1.6-5.4 lbs./hr., 0.73-2.45 kg/hr | | .045 in., 1.2 mm | 140-280 ipm, 356-711 cm/min | 100-210 | 17-22 | 2.4-6.0 lbs./hr., 1.09-2.72 kg/hr |
Spray Arc Transfer Table | .030 in., 0.8 mm | 265-550 ipm, 673-1397 cm/min | 160-210 | 24-28 | 6.5-9.6 lbs./hr., 2.95-4.35 kg./hr. | | .035 in., 0.9 mm | 240-468 ipm, 610-1189 cm/min | 170-255 | 24-30 | 7.8-12.7 lbs./hr., 3.54-5.76 kg./hr. | | .045 in., 1.2 mm | 192-360 ipm, 488-914 cm/min | 200-300 | 24-30 | 6.8-13.6 lbs./hr., 3.08-6.17 kg./hr. | | .062 in., 1.6 mm | 120-192 ipm, 305-488 cm/min | 215-325 | 24-32 | 7.3-14.5 lbs./hr., 3.31-6.58 kg./hr. |
Properties:
| GTAW using 100% Argon | | | Yield Strength | 60 ksi, 410 MPa | | Tensile Strength | 88 ksi, 605 MPa | | Elongation in 2" | 43 % | | Impact Toughness at -320ºF (-196ºC) | | | Absorbed Energy | 80 ft.-lbs., 110 J | | Lateral Expansion | 53 mils, 1.35 mm | | Typical Chemical Analysis | | | C | 0.015 % | | Mn | 1.7 % | | Si | 0.45 % | | S | 0.01 % | | Cr | 20 % | | Ni | 10 % | | Mo | 0.1 % | | Cu | 0.15 % | | Ferrite | 9 FN |