ESAB Arcaloy ER308L Si Welding Wire - .052" - 33 lb BAWS - 258171131

OK Arcaloy ER308LSi is a continuous, solid, corrosion-resistant, chromium-nickel wire for welding austenitic chromium-nickel alloys of the 18 Cr- 8% Ni type. The alloy has a low carbon content, making it particularly recommended where there is a risk of intergranular corrosion.

* This item is subject to Industry Alloy Surcharges

Classifications/Approvals
- AWS A5.9; ER308Si/ER308LSi
- Certified by CWB - AWS A5.9
- ASME II SFA 5.9 ER308Si/308LSi
- ASME IX F No. 6

Depositions/Parameters:

Short Circuit Transfer Table
Diameter	Wire Feed Speed	Amps	Volts	Deposition Rate
.030 in., 0.8 mm	156-312 ipm, 396-792 cm/min	40-120	15-20	1.4-3.8 lbs./hr., 0.64-1.72 kg/hr
.035 in., 0.9 mm	156-312 ipm, 396-792 cm/min	60-140	15-21	1.6-5.4 lbs./hr., 0.73-2.45 kg/hr
.045 in., 1.2 mm	140-280 ipm, 356-711 cm/min	100-210	17-22	2.4-6.0 lbs./hr., 1.09-2.72 kg/hr

Spray Arc Transfer Table
Diameter	Wire Feed Speed	Amps	Volts	Deposition Rate
.030 in., 0.8 mm	265-550 ipm, 673-1397 cm/min	160-210	24-28	6.5-9.6 lbs./hr., 2.95-4.35 kg/hr
.035 in., 0.9 mm	240-468 ipm, 610-1189 cm/min	170-255	24-30	7.8-12.7 lbs./hr., 3.54-5.76 kg/hr
.045 in., 1.2 mm	192-360 ipm, 488-914 cm/min	200-300	24-30	6.8-13.6 lbs./hr., 3.08-6.17 kg/hr
.062 in., 1.6 mm	120-192 ipm, 305-488 cm/min	215-325	24-32	7.3-14.5 lbs./hr., 3.31-6.58 kg/hr

Properties:

GMAW using 98% Argon / 2% Oxygen
Yield Stress	55 ksi, 380 MPa
Tensile Strength	85 ksi, 690 MPa
Elongation in 2"	40 %
Typical Chemical Analysis
C	0.015 %
Mn	1.7 %
Si	0.8 %
S	0.01 %
Cr	20 %
Ni	10 %
Mo	0.1 %
Cu	0.2 %
Ferrite	10 FN